CORRISPONDENZA DESIGNAZIONI INTERNAZIONALI
| QUALITÀ | EUROPA | GERMANIA | FRANCIA | SPAGNA | G.B. | USA | |
|---|---|---|---|---|---|---|---|
| EN | DIN | W.n. | AFNOR | UNE | B.S. | AISI/SAE | |
| AISI 4130 | 25/30CrMo4 | 1.7218 | 708A25 | 4130 | |||
ANALISI CHIMICA
| DESIGNAZIONE ACCIAIO | COMPOSIZIONE CHIMICA | ||||||||
|---|---|---|---|---|---|---|---|---|---|
| SIMBOLICA | C | Mn | Si | P max |
S max |
Cr | Mo | V | Al max |
| AISI 4130 | 0,28 ÷ 0,33 | 0,40 ÷ 0,60 | 0,15 ÷ 0,35 | 0,035 | 0,040 | 0,60 ÷ 1,10 | 0,15 ÷ 0,25 | - | - |
CARATTERISTICHE MECCANICHE
| ACCIAIO | d ≤ 16mm | 16mm < d ≤ 40mm | 40mm < d ≤ 100mm | 100mm < d ≤ 160mm | |||||||||||||
| SIMBOLICA | NUMERICA | Re min | Rm | A min | KCU min | Re min | Rm | A min | KCU min | Re min | Rm | A min | KCU min | Re min | Rm | A min | KCU min |
| N/mm2 | % | J | N/mm2 | % | J | N/mm2 | % | J | N/mm2 | % | J | ||||||
| AISI 4130 | 1,7218 | 685 | 880 ÷ 1080 |
12 | 32,5 | 635 | 830 ÷ 1030 |
12 | 32,5 | 520 | 740 ÷ 880 |
13 | 30 | 420 | 690 ÷ 830 |
15 | 30 |
TEMPRABILITÀ JOMINY
| DESIGNAZIONE ACCIAIO | LIMITI DELLA GAMMA | DUREZZA HRC AD UNA DISTANZA DALL'ESTREMITÀ TEMPRATA DELLA PROVETTA PARI AI SEGUENTI VALORI (MM) | |||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| SIMBOLICA | NUMERICA | 1,5 | 3 | 5 | 7 | 9 | 11 | 13 | 15 | 20 | 25 | 30 | 35 | 40 | |
| AISI 4130 | 1.7218 | max | 56 | 55 | 53 | 51 | 49 | 47 | 45 | 42 | 39 |
37 |
35 | 33 | 32 |
| min | 46 | 45 | 42 | 38 | 35 | 30 | 28 | 26 | 24 | 23 | 21 | 20 | - | ||
NORMALMENTE DISPONIBILE A MAGAZZINO
| COLORAZIONE M.T. | QUALITÀ | TRATTAMENTO TERMICO | STATO SUPERFICIALE | DIAMETRO (mm) |
|---|---|---|---|---|
| AISI 4130 | Bonificato | laminato | 80-350 |
 |
Scarica la scheda tecnica |