PROPRIETÀ ED IMPIEGHI
È L’ACCIAIO DA BONIFICA PIÙ USATO PER L’OTTIMO RAPPORTO CARATTERISTICHE/COSTO. POSSIEDE UN’ELEVATA TEMPRABILITÀ, BUONA RESISTENZA A CALDO, OTTIMA FUCINABILITÀ E BUONA LAVORABILITÀ ALLE MACCHINE.
PUÒ ESSERE TEMPRATO IN SUPERFICIE O NITRURATO PER ELEVARE LA RESISTENZA ALL'USURA E ALLA FATICA.
INGRANAGGI BONIFICATI E NITRURATI POSSONO SOSTITUIRE QUELLI CEMENTATI E TEMPRATI, SE NON SOTTOPOSTI A PRESSIONI SPECIFICHE ECCESSIVAMENTE ELEVATE.
CORRISPONDENZA DESIGNAZIONI INTERNAZIONALI
| QUALITÀ | EUROPA | GERMANIA | FRANCIA | SPAGNA | G.B. | USA | |
|---|---|---|---|---|---|---|---|
| EN | DIN | W.n. | AFNOR | UNE | B.S. | AISI/SAE | |
| 42CrMo4 | 42CrMo4 | 42CrMo4 | 1,7225 | 42CD4 | F1252 | 708M40 | 4140 |
COMPOSIZIONE CHIMICA % (EN 10083-3)
| DESIGNAZIONE ACCIAIO | COMPOSIZIONE CHIMICA | |||||||||
|---|---|---|---|---|---|---|---|---|---|---|
| SIMBOLICA | NUMERICA | C |
Si max |
Mn |
P max |
S | Cr | Mo | Ni | V |
| 42CrMo4 | 1,7225 | 0,38 ÷ 0,45 | 0,40 | 0,60 ÷ 0,90 | 0,025 | max. 0,035 | 0,90 ÷ 1,20 | 0,15 ÷ 0,30 | - | - |
| 42CrMoS4 | 1,7227 | 0,020 ÷ 0,040 | ||||||||
I LIMITI DI CONCENTRAZIONE DEGLI ELEMENTI NON INDICATI IN TABELLA SONO DESUMIBILI DALLA NORMA EN 10020.
CARATTERISTICHE MECCANICHE (EN 10083-3)
| ACCIAIO | CARATTERISTICHE MECCANICHE PER LA SEZIONE RIDOTTA (EN 10083-1:2006, ALLEGATO A) CON UN DIAMETRO (D) DI | |||||||||||||||||||||||||
| d ≤ 16mm | 16mm < d ≤ 40mm | 40mm < d ≤ 100mm | 100mm < d ≤ 160mm | 160mm < d ≤ 250mm | ||||||||||||||||||||||
| SIMBOLICA | NUMERICA | Re min | Rm | A min | Z min | KVb min | Re min | Rm | A min | Z min | KVb min | Re min | Rm | A min | Z min | KVb min | Re min | Rm | A min | Z min | KVb min | Re min | Rm | A min | Z min | KVb min |
| N/mm2 | % | % | J | N/mm2 | % | % | J | N/mm2 | % | % | J | N/mm2 | % | % | J | N/mm2 | % | % | J | |||||||
| 42CrMo4 | 1,7225 | 900 |
1100 to 1300 |
10 | 40 | - | 750 |
1000 to 1200 |
11 | 45 | 35 | 650 |
900 to 1100 |
12 | 50 | 35 | 550 |
800 to 950 |
13 | 50 | 35 | 500 |
750 to 900 |
14 | 55 | 35 |
| 42CrMoS4 | 1,7227 | |||||||||||||||||||||||||
TEMPRABILITÀ JOMINY (EN 10083-3)
| DESIGNAZIONE ACCIAIO | SIMBOLO | LIMITI DELLA GAMMA | DUREZZA HRC AD UNA DISTANZA DALL'ESTREMITÀ TEMPRATA DELLA PROVETTA PARI AI SEGUENTI VALORI (MM) | |||||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| SIMBOLICA | NUMERICA | 1,5 | 3 | 5 | 7 | 9 | 11 | 13 | 15 | 20 | 25 | 30 | 35 | 40 | 45 | 50 | ||
| 42CrMo4 | 1,7225 | +H | max | 61 | 61 | 61 | 60 | 60 | 59 | 59 | 58 | 56 | 53 | 51 | 48 | 47 | 46 | 45 |
| 42CrMoS4 | 1,7227 | +H | min | 53 | 53 | 52 | 51 | 49 | 43 | 40 | 37 | 34 | 32 | 31 | 30 | 30 | 29 | 29 |
NORMALMENTE DISPONIBILE A MAGAZZINO
| COLORAZIONE M.T. | QUALITÀ | TRATTAMENTO TERMICO | STATO SUPERFICIALE | DIAMETRO (mm) |
|---|---|---|---|---|
 |
42CrMo4 | Bonificato |
laminato rullato forgiato tornito pelato h11 / trafilato |
80-330 340-800 20-80 |
 |
42CrMo4 |
Bonificato |
laminato rullato laminato sgrossato |
80-320 |
 |
Scarica la scheda tecnica |