ENTSPRECHUNG DER INTERNATIONALEN BESTIMMUNGEN
| QUALITÄT | EUROPA | DEUTSCHLAND | FRANKREICH | SPANIEN | G.B. | USA | |
|---|---|---|---|---|---|---|---|
| EN | DIN | W.n. | AFNOR | UNE | B.S. | AISI/SAE | |
| S355J2 | 10025-2:2004 | 1,0577 | |||||
CHEMISCHE ZUSAMMENSETZUNG % (EN 10025)
| STAHLBEZEICHNUNG | CHEMISCHE ZUSAMMENSETZUNG | |||||||||
|---|---|---|---|---|---|---|---|---|---|---|
| SYMBOLISCH | NUMERISCH | C max |
Si max |
Mn max |
P max |
S max |
Cr | Mo | Ni | Cu Max |
| S355J2 | 1,0577 | 0,20 | 0,55 | 1,60 | 0,025 | 0,025 | - | - | - | 0,40 |
MECHANISCHE EIGENSCHAFTEN WARM GEWALZT (EN 10025)
| STAHL | 3mm < d ≤ 100mm | 100mm < d ≤ 150mm | 150mm < d ≤ 250mm | 250mm < d ≤ 400mm | |||||
| SYMBOLISCH | NUMERISCH | Rm | HB | Rm | HB | Rm | HB | Rm | HB |
| N/mm2 | N/mm2 | N/mm2 | N/mm2 | ||||||
| S355J2 | 1,0577 | 470 to 630 |
141 to 192 |
450 to 600 |
135 to 178 |
450 to 600 |
135 to 178 |
450 to 600 |
135 to 178 |
MECHANISCHE EIGENSCHAFTEN KALT GEZOGEN +C (EN10277-2:2008)
| STAHL | 5mm < d ≤ 10mm | 10mm < d ≤ 16mm | 16mm < d ≤ 40mm | 40mm < d ≤ 63mm | 63mm < d ≤ 100mm | ||||||||||||||||
| SYMBOLISCH | NUMERISCH | Re min | Rm | A min | HB | Re min | Rm | A min | HB | Re min | Rm | A min | HB | Re min | Rm | A min | HB | Re min | Rm | A min | HB |
| MPa | % | MPa | % | MPa | % | MPa | % | MPa | % | ||||||||||||
| S355J2C | 1,0579 | 520 | 630 to 950 |
6 | 192 to 286 |
450 | 580 to 880 |
7 | 172 to 263 |
350 | 530 to 880 |
8 | 156 to 253 |
335 | 500 to 770 |
9 | 152 to 231 |
315 | 470 to 740 |
9 | 141 to 224 |
NORMALERWEISE AB LAGER LIEFERBAR
| M.T. FÄRBUNG | QUALITÄT | WÄRMEBEHANDLUNG | OBERFLÄCHE | DURCHMESSER (mm) |
|---|---|---|---|---|
| S355J2 | Normalisiert | gewalzt geschmiedet gedreht gezogen |
30-300 310-520 3-100 |