CORRESPONDENCE TO INTERNATIONAL DESIGNATIONS
QUALITY | EUROPE | GERMANY | FRANCE | SPAIN | G.B. | USA | |
---|---|---|---|---|---|---|---|
EN | DIN | W.n. | AFNOR | UNE | B.S. | AISI/SAE | |
ASTM A350 - LF2 | S355J2G3~ | St52.3~ | EN50D | LF2 |
CHEMICAL ANALYSIS (ASTM A350M-07)
STEEL DESIGNATION | CHEMICAL COMPOSITION | ||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|
SYMBOLIC |
C max |
Mn | Si |
P max |
S max |
Cr max |
Mo max |
Cu max |
Ni max |
V max |
Nb max |
ASTM A350 - LF2 | 0,30 | 0,60 ÷ 1,35 | 0,15 ÷ 0,30 | 0,035 | 0,040 | 0,30 | 0,12 | 0,40 | 0,40 | 0,08 | 0,02 |
MECHANICAL CHARACTERISTICS (ASTM A350M-07)
STEEL | ||||||
SYMBOLIC | NUMERIC | Re min | Rm | A min | Z min | Kv -46°C cl.1 |
N/mm2 | % | % | J | |||
ASTM A350 - LF2 | 250 |
485 ÷ 655 |
22 | 30 | 27 |
USUALLY AVAILABLE EX STOCK
M.T. COLORATION | QUALITY | HEAT TREATMENT | SURFACE | DIAMETER (mm) |
---|---|---|---|---|
ASTM A350 - LF2 | Normalised |
rolled peeled h13 forged turned |
40-300 90-280 300-530 |
Download technical sheet |
CORRESPONDENCE TO INTERNATIONAL DESIGNATIONS
QUALITY | EUROPE | GERMANY | FRANCE | SPAIN | G.B. | USA | |
---|---|---|---|---|---|---|---|
EN | DIN | W.n. | AFNOR | UNE | B.S. | AISI/SAE | |
AISI 4130 | 25/30CrMo4 | 1.7218 | 708A25 | 4130 |
CHEMICAL ANALYSIS
STEEL DESIGNATION | CHEMICAL ANALYSIS | ||||||||
---|---|---|---|---|---|---|---|---|---|
SYMBOLIC | C | Mn | Si | P max |
S max |
Cr | Mo | V | Al max |
AISI 4130 | 0,28 ÷ 0,33 | 0,40 ÷ 0,60 | 0,15 ÷ 0,35 | 0,035 | 0,040 | 0,60 ÷ 1,10 | 0,15 ÷ 0,25 | - | - |
MECHANICAL CHARACTERISTICS
STEEL | d ≤ 16mm | 16mm < d ≤ 40mm | 40mm < d ≤ 100mm | 100mm < d ≤ 160mm | |||||||||||||
SYMBOLIC | NUMERIC | Re min | Rm | A min | KCU min | Re min | Rm | A min | KCU min | Re min | Rm | A min | KCU min | Re min | Rm | A min | KCU min |
N/mm2 | % | J | N/mm2 | % | J | N/mm2 | % | J | N/mm2 | % | J | ||||||
AISI 4130 | 1,7218 | 685 | 880 ÷ 1080 |
12 | 32,5 | 635 | 830 ÷ 1030 |
12 | 32,5 | 520 | 740 ÷ 880 |
13 | 30 | 420 | 690 ÷ 830 |
15 | 30 |
JOMINY HARDENABILITY
STEEL DESIGNATION | RANGE LIMITS | HRC HARDNESS MEASURED FROM THE QUENCHED END OF THE TEST TUBE (MM) | |||||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
SYMBOLIC | NUMERIC | 1,5 | 3 | 5 | 7 | 9 | 11 | 13 | 15 | 20 | 25 | 30 | 35 | 40 | |
AISI 4130 | 1.7218 | max | 56 | 55 | 53 | 51 | 49 | 47 | 45 | 42 | 39 |
37 |
35 | 33 | 32 |
min | 46 | 45 | 42 | 38 | 35 | 30 | 28 | 26 | 24 | 23 | 21 | 20 | - |
USUALLY AVAILABLE EX STOCK
M.T. COLORATION | QUALITY | HEAT TREATMENT | SURFACE | DIAMETER (mm) |
---|---|---|---|---|
AISI 4130 | Quenched and tempered | rolled | 80-350 |
Download technical sheet |
CORRESPONDENCE TO INTERNATIONAL DESIGNATIONS
QUALITY | EUROPE | GERMANY | FRANCE | SPAIN | G.B. | USA | |
---|---|---|---|---|---|---|---|
EN | DIN | W.n. | AFNOR | UNE | B.S. | AISI/SAE | |
4140 | 1,7225 | 708M40 | 4140 |
CHEMICAL ANALYSIS %
STEEL DESIGNATION | CHEMICAL ANALYSIS | |||||||||
---|---|---|---|---|---|---|---|---|---|---|
SYMBOLIC | NUMERIC | C | Mn | Si |
P max |
S max |
Cr | Mo | Ni | V |
AISI 4140 | 1,7225 | 0,38 ÷ 0,43 | 0,75 ÷ 1,00 | 0,15 ÷ 0,35 | 0,035 | 0,040 | 0,80 ÷ 1,10 | 0,15 ÷ 0,25 | - | - |
CONCENTRATION LIMITS OF THE ELEMENTS THAT ARE NOT INDICATED IN THE TABLE CAN BE DEDUCED IN THE EN 10020 REGULATION.
MECHANICAL CHARACTERISTICS
STEEL | NORMALISATION TEMPERATURE 900°C MIN – TEMPERING TEMPERATURE 620°C MIN | ||||||
SYMBOLIC | NUMERICA | Re min | Rm min | A min | Z min | Durezza HB | KV a -46°C min |
N/mm2 | % | % | max | J | |||
AISI 4140 | 1,7225 | 520 | 677 | 20 | 45 | 237 | 27 |
USUALLY AVAILABLE EX STOCK
M.T. COLORATION | QUALITY | HEAT TREATMENT | SURFACE | DIAMETER (mm) |
---|---|---|---|---|
Aisi 4140 | Quenched and tempered | rolled | 30-300 |
Download technical sheet |
CORRESPONDENCE TO INTERNATIONAL DESIGNATIONS
QUALITY | EUROPE | GERMANY | FRANCE | SPAIN | G.B. | USA | |
---|---|---|---|---|---|---|---|
EN | DIN | W.n. | AFNOR | UNE | B.S. | AISI/SAE | |
B16 | 40CrMoV4-6 | 40CrMoV4-6 | 40CrMoV4-6 | 1506-661 | ASTM-A193 B16 |
CHEMICAL ANALYSIS (ASTM A193)
STEEL DESIGNATION | CHEMICAL COMPOSITION | ||||||||
---|---|---|---|---|---|---|---|---|---|
SYMBOLIC | C | Mn | Si |
P max |
S max |
Cr | Mo | V |
Al max |
B16 | 0,36 ÷ 0,47 | 0,45 ÷ 0,70 | 0,15 ÷ 0,35 | 0,035 | 0,040 | 0,80 ÷ 1,15 | 0,50 ÷ 0,65 | 0,25 ÷ 0,35 | 0,015 |
CONCENTRATION LIMITS OF THE ELEMENTS THAT ARE NOT INDICATED IN THE TABLE CAN BE DEDUCED IN THE EN 10020 REGULATION.
MECHANICAL CHARACTERISTICS
STEEL | NORMALISATION TEMPERATURE 900°C MIN – TEMPERING TEMPERATURE 620°C MIN | |||||
SYMBOLIC | Re min | Rm min | A min | Z min | Hardness HB max | |
N/mm2 | % | % | J | |||
B16 | 655 | 760 | 17 | 45 | 321 |
USUALLY AVAILABLE EX STOCK
M.T. COLORATION | QUALITY | HEAT TREATMENT | SURFACE | DIAMETER (mm) |
---|---|---|---|---|
B16 (40CrMoV4-6) | Quenched and tempered | rolled | 70-150 |
Download technical sheet |
HOT WORK CREEP STEELS ARE STEELS THAT HAVE TO RESIST PLASTIC DEFORMATION OVER TIME AT HIGH TEMPERATURES (FROM 350° TO 700°C). THESE STEELS ARE EMPLOYED FOR THE CONSTRUCTION OF VALVES, FLANGES, TIE RODS, TUBES, PLATES ETC. FOR THE CHEMICAL INDUSTRY, PETROCHEMICAL INDUSTRY, THERMAL AND NUCLEAR POWER PLANTS, OVERHEATED STEAM CONVEYORS, ROTORS AND PIPINGS THAT TRANSPORT HOT FLUIDS UNDER PRESSURE. THE SPECIFIC EMPLOYMENTS OF THESE STEELS REQUIRE AN ELEVATED WELDABILITY, FOR THIS REASON THEY ALL HAVE A LOW CARBON CONTENT (MAX. 0,20%).
WE CAN PROVIDE FORGED PARTS WITH SPECIFIC DESIGN UP TO 1000 KG OF WEIGHT WITH MAXIMUM Ø 700 MM.